EW Polymer Group

Articles

Butyl Rubber

CENWAY CI IR 1301

Composition
Copolymer rubber of Chlorinated Isobutylene-Isoprene with low mooney viscosity.

Basic Properties

PropertiesUnitIndexTest Method
Product Form   Off-white Visual
Mooney Viscosity (ML1+8,125℃) MU 38±5 ISO 289/ASTM D1646
Volatile Matter wt% ≤0.7 ISO 248/ASTM D5668
Chlorine Content wt% 1.2±0.2 CENWAY METHOD
Total Ash wt% ≤0.7 ISO 247/ASTM D5667
Antioxidant (non-staining) wt% ≥0.02 CENWAY METHOD

Cure Characteristics

PropertiesUnitIndexTest Method
FL dN•m 2.5±0.9 ISO 6502/ASTM D5289
FH dN•m 8.0±1.5 ISO 6502/ASTM D5289
ts1 min 1.2±0.9 Rotorless cur (MDR)
tc50 min 3.0±2.0 160℃×40min,0.5°arc
tc90 min 8.5±3.3 160℃×40min,0.5°arc
Test Formulation ISO 7663/ASTM D 3958 CI IR1301 100, IRB#7 40, Zn0 5, St.A 1

 Applications
Chlorobutyl Rubber CI IR 1301 has superior air impermeability, outstanding performance of heat-resistance, chemical corrosion-resistance, thermal aging resistance, and good curing performance. It can be widely used for tire inner liners, medical stoppers, corrosion-resistance lining, protective clothing, shoes production and TPV industry.

Safety & Toxicity
CI IR 1301 is polymer in solid with stable performance. It is harmless and not dangerous for humans, plants and animals. For relevant safety data and reference, please refer to MSDS.

Packaging
25 ± 0.5 kg/bale in EVA film.
Pallets of plywood box of 1050 kg with 42 bales.
Pallets of metal box of 1200 kg with 48 bales.

Storage Life & Conditions
Two years with keeping storage & transport under 35℃ and against sunlight.